XINGFA UPVC Trapezium Roof Sheet Specification
Width: 890mm/1029mm
Effective Width: 890mm/1029mm
Length: Customized
Thickness: 1.5mm
Application: Sheds, Workshops, Parking Lots, Production Workshops, Greenhouses, Farms, Chemical Plants, ect.
UPVC Roof Sheet in Trapezium 890
Brand: XINGFA
Thickness：1.5mm
Width：890mm/1029mm
Color: White
Layers: 3 Layers
Supply Type: OEM/ODM
Delivery Time: 10-15 Working days after advance
MOQ: 2000 square meters
Warranty: 10 years
16
People watching this product now!
Description
UPVC Roof Sheet in Trapezium 890mm/1029mm
Over the past two decades, PVC roof panels have already been utilized in various kinds of business and gardening components around the globe.
From hog barns to dairy food storage sheds or poultry properties, vehicle washes, substance-finalizing plants and flowers, or fertilizer-storing establishments.
Due to its strength and durability, PVC roof panels typically have a long service life. In addition, Corrugated plastic roofing sheets are easy to install using regular resources.
| Test Technical Data from SGS | ||||||||||||||||
| Item | Test Method | Test Condition | Result | |||||||||||||
| Vicat Softening temperature | ASTM D1525-17E1 | Specimen thickness: 3.70mm (3 layers plied up) Heat-transfer media: Silicone oil Rate of temperature:50℃/h Load:50N | 79.9℃ | |||||||||||||
| Muriatic acid resistance | ISO 175-2010 | Immersion method Test time: 48h | 35%(m/m)HCL(AR) | No visial change | ||||||||||||
| Sulfuric acid resistance | ISO 175-2010 | Immersion method Test time: 48h | 30%(m/m)H2SO4(AR) | No visial change | ||||||||||||
| Alkali resistance | ISO 175-2010 | Immersion method Test time: 48h | 40%(m/m)NaOH(AR) | No visial change | ||||||||||||
| Xenon-arc Exposure | ISO4892-2:2013 ISO 105-A02:1993/Cor.2:2005 ASTM D2244-11 | Irradiance:(0.51±0.02)W/(m2·nm)@340nm 102 min light at (63±3)℃ BPT， (50±10)% RH 18 min light and water spray Filter: Boro/Boro Exposure Period: 500h | Grey Scale: 2-3 △Eab=3.5 | |||||||||||||
| Flexural strength | ISO 790-17 Procedure A | Testing speed: 0.9mm/min Span: 25.4mm | 84.5Mpa | |||||||||||||
| Striker Impacted by a Falling Weight | ASTM D4226-19E1 Procedure B | Specimen thickness: 9.96mm Geometry: H.25 Strike weight:3.6kg | Mean failure energy: 6.7J | |||||||||||||
| Tensile Strength | ASTM D638-14 | Specimen thickness: 1.31mm Testing speed: 50mm/min Distance between grips: 115mm | 34.5Mpa | |||||||||||||