Brand: XINGFA
Thickness：1.5mm,2.0mm,2.3mm,2.5m,2.8mm,3.0mm
Width：1130mm
Color: White
Layers: 3 Layers
Supply Type: OEM/ODM
Delivery Time: 10-15 Working days after advance
MOQ: 2000 square meters
Warranty: 10 years
Waterproof Shed Cheap Plastic Roofing Sheets
XINGFA UPVC Trapezoidal T1130 Specification
Width: 1130mm
Effective Width: 1050mm
Length: Customized
Thickness: 1.5mm,2.0mm,2.3mm,2.5m,2.8mm,3.0mm
Application: Sheds, Workshops, Parking Lots, Production Workshops, Greenhouses, Farms, Chemical Plants, ect.
UPVC Trapezoidal Roof Sheet T1130
Over the past two decades, PVC roof panels have already been utilized in various kinds of business and gardening components around the globe.
From hog barns to dairy food storage sheds or poultry properties, vehicle washes, substance-finalizing plants and flowers, or fertilizer-storing establishments.
Due to its strength and durability, PVC roof panels typically have a long service life. In addition, Corrugated plastic roofing sheets are easy to install using regular resources.
| Test Technical Data from SGS | ||||||||||||||||
| Item | Test Method | Test Condition | Result | |||||||||||||
| Dimensional Stability | ASTM D1204-14 | Specimen: 25cm*25cm 100℃, 60min Medium: Talc powder | Direction of Vertical | -0.60% | ||||||||||||
| Direction of Horizontal | 1.60% | |||||||||||||||
| Vicat Softening temperature | ISO 306-2013 method B50 | Heat-transfer meida: Silicone oil Rate of temperature: 50K/h Load: 50N | 77.0℃ | |||||||||||||
| Fire rating | DIN 4102-1:1998-05 | Cotton indicator ignited by flaming particles or drops with V-2 | B2 | |||||||||||||
| Effect of liquid chemicals | ISO 175-2010 | Immersion method Temperature: 23℃ Immersion time: 48h | 40%(m/m)NaOH | No visual change | ||||||||||||
| 35%(m/m)HCL | Visual discoloring, but no other visual change | |||||||||||||||
| 30%(m/m)H2SO4 | No visual change | |||||||||||||||
| Light Ageing Test Xenon-arc Exposure | ISO4892-2:2013cycle4 ISO 105-A02:1993/Cor.2:2005 ASTM D2244-15a | Irradiance:(0.51±0.02)W/(m·nm)@340nm 102 min light at (63±3)℃ BPT， (50±10)% RH 18 min light and water spray Filter: Boro/Boro Exposure Period: 1000h | Grey Scale: 3 △Eab=1.3 | |||||||||||||
| Striker Impacted by a Falling Weight | GB/T 8814-2004 Section 5.7 Section 6.7 | Condition: -10℃ , 1h →Take out and do the test within 10s Strik weight:1000g Height:1000mm Span:200mm No. of specimen tested:10 | breakage:0 | |||||||||||||
| Thermal conductivity | ASTM C518-17 | Condition the test specimen at(23+2)°C and(50+5)% relative humidity to constant mass | 0.09（W/m·K) | |||||||||||||
| Thermal resistance | 0.03(m2·K)/W | |||||||||||||||
| Tensile Breaking strength | GB/T 1040.2-2006 | Span：115mm Specimen width: 25mm Power: 1050N | 20.3Mpa | |||||||||||||
| Tensile Strength | GB/T 1040.2-2006 | Span：115mm Specimen width: 25mm Power: 1050N | 20.63Mpa | |||||||||||||