UPVC Trapezium Roof Sheet T1130

Product Parameter
Model: T1130
Width: 1130mm
Efficient width: 1050mm
Thickness: 1.5mm,2.0mm,2.5mm,3.0mm
Length: Customized (20'container 5.8 meter, 40'container 11.8 meter)
Applications: factory roof, warehouse roof, wall panel etc...
Surface finishing: ASA coated,Embossed type,standard type.
Layer: Single layer, Three layers, Four layers

FLLOW US:

INQUIRY

PRODUCT DETAILS

Features

Fireproof
Acid and alkali resistance
Toughness
Weather resistance
Low noise
Portability
Environmental protection

UPVC Trapezium Roof Sheet T1130upvc-roof-color
UPVC Trapezium Roof Sheet 07Foshan Ceramic Factory
UPVC Trapezium Roof Sheet 08Foshan Ceramic Factory

UPVC TEST REPORT

Num.

Test item

Test method

The test condition

Test result

1

Tensile strength

ISO 527-1:2012 & ISO 527 -2:2012

Testing speed: 50mm/min

23.1 Mpa

2

Flexural strength

ISO 178:2010/Amd.1:2013 Method A

Test speed: 1mm/min

50.9 Mpa

3

Impact Resistance

With reference to GB/T 8814-2004 Section 5.7, Section 6.7 and client’s requirement

-10°C, 1h

Strike weight:1000g

Height:1000mm

Number of specimen failures: 0

4

Vicat Softening Temperature

ISO 306:2013 Method B 50

Rate of temperature: 50K/h

77.0°C

5

Effects of liquid chemicals

ISO 175:2010

Temperature: 23°C

Immersion time:48h

40%(m/m) NaOH

No visual change

ISO 175:2010

Temperature: 23°C

Immersion time:48h

35%(m/m) HCl

Visual discoloring, but no other visual change

ISO 175:2010

Temperature: 23°C

Immersion time:48h

30%(m/m)H2SO4

No visual change

6

Light Ageing Test – Xenon-arc Exposure

ISO 4892-2:2013 cycle 4 & ISO 105-A02:1993/Cor.2:2005 & ASTM D2244– 15a

Exposure period: 1000h

Grey scale: 3

△E*ab : 1.3

7

Dimensional Stability

With reference to ASTM D1204-14 and client’s requirement

100℃,60min→23±2℃, 50±5% RH, 60min

Direction of arrow: -0.6%

Perpendicular to Direction of arrow: 1.6%

NO.

Test item

Test method

Test condition

Result

1

Tensile strength

ASTM D638-03

Specimen: Type I

Speed: 50mm/min

Before aging

29.2 MPa

After aging

36.9MPa

2

Flexural strength

ASTM D790-07 Procedure A and client’s requirement

127x13.07x1.98mm

Speed: 0.8mm/min

Span: 30mm

Before aging

59.3MPa

After aging

62.8MPa

3

Thermal Conductivity [W/(m·K)]

ASTM C518-04

----

0.08846

4

Coeffcient of Linear Thermal Expansion(μm/m·℃)

Rf.ASTM D696-03

---

49.68

5

Vertical Burning

UL 94-1996REV.9:2006 section 8

Specimen: 129x12.9x1.99mm

V-0

6

Oxygen Index

ASTM D2863-06a

Specimen:Type III

Thickness: 1.97mm

Ignition prceduce: Method A

36.3%

7

Water absorption

ASTM D570-98(2005)

Drying :50℃,24h

Immersion: 23℃,24h

0.04%

8

 Vicat softening temperature

ASTM D1525-06

Thickness: 3.92mm

2pcs plied up

Rate of temperature rise: 50℃/h

Load: 1.82MPa

90.0℃

9

Heat deflection temperature

ASTM D648-07 Method B

Width: 12.83mm

Depth: 3.73mm

Heating rate: 120℃/h

Load:1.82MPa

55.6℃

10

High temperature

Supplied by client

60℃,6h

No visible change

11

Impact resistance (Gardner impact)

ASTM D5420-04

Statement of geometry: GE(striker:φ16.26mm)

Thickness:2.00mm

Mean-failure energy 6J

12

Low temperature resistance

Supplied by client

-35℃,6h

 

No visible change

 

13

Chemical resistance

Supplied by client

70% Ethanol Solution, (m/m),23℃,2h

No visible change

10% NaOH Solution, (m/m),23℃,2h

No visible change

Saturation NaCI Solution 23℃,2h

No visible change

14

UV Exposure

ASTM G154-06 Cycle 1,ISO 105-A02:1993

8h UV at(60±3)℃BPT, 0.89W/(m2·nm)@340nm 4h condensation at (50±3)℃BPT Exposure period:1000h

Grey scale: 3

contact us

contact-email
contact-logo

Foshan Chancheng Xingfa Tile Industry Co.,Ltd

We provide high-quality products & services to our clients

看不清,请点击我!

If you would like to leave us a comment please go to contact us

Telphone: +86-757-85330625

email: info@upvcsupplier.com

contact-clo
top