UPVC Wall Panel W1130

UPVC Wall Panel W1130

Product Parameter
Model: W1130
Width: 1130mm
Efficient width: 1080mm
Thickness: 1.5mm,2.0mm,2.5mm,3.0mm
Length: Customized (20'container 5.8 meter, 40'container 11.8 meter)
Applications: factory roof, warehouse roof, wall panel etc...
Surface finishing: ASA coated,Embossed type,standard type.
Layer: Single layer, Three layers, Four layers

FLLOW US:

INQUIRY

PRODUCT DETAILS

Features


Excellent anti-load Capacity
Good Sound Insulation
Excellent Corrosion Resistance
Good shock Resistance
Low Temperature Resistance
Excellent Self-cleaning
Excellent Heat Insulation
Volume Stability
Excellent Water Resistance
Strong Fire Retardant
Excellent Insulation
Environment Protection
Rapid Installation

------bai.jpg

 
 
 

ASA Synthetic resin Roof Tile Test Result From SGS

NO.

Test item

Test method

Result

1

Color persistence

ISO

4892-2:2013,ISO105-A02:199

3 Cor2:2005 and ASTM

D2244-11

△E≤5

2

Muriatic acid resistance

ISO175-2010

No visible change

3

Sulfuric acid resistance

ISO175-2010

No visible change

4

Alkali resistance

ISO175-2010

No visible change

5

Tensile strength

ISO 527-1:2012 and ISO527-2:2012

20.3MPa

6

Nominal tensile strain at break

ISO 527-1:2012 and ISO527-2:2012

13%

7

Flexural strength

ISO 178:2010 / Amd.1:2013

Method A

41.3MPa

8

Impact resistance

GB/T 8814-2004 Section

5.7 and 6.7

-10℃,hammering,intact

9

Oxygen Index

ISO 4589-1:1996 and ISO

4589-2:1996 / Amd.1:2005

32.80%

10

Burning test

DIN 4102-1:1998-05

B1

ASA Synthetic resin Roof Tile Test Result From SGS (2014)

NO.

Test item

Test method

Test condition

Test result

1

Xenon-arc Exposure

ISO 4892-2:2013,ISO 105-A02:1993 

Cor2: 2005 and ASTM D2244-11

ISO 4892-2:2013 cycle 4 Irradiance:(0.51±0.02)W/(m2·nm)@340nm 102min light at (63±3)℃BPT,(50±10)℃RH

18min light and water sparay Filter: Boro / Boro

Exposure period: 500h

Greyscale

2-3

∆E*ab

3.5

2

Thermal resistance

With reference to ASTM D3045-92(2010) and client’s requirements

150℃.30min

Visible deformation and color fading, but o other visible change.

3

Muriatic acid resistance

With reference to ISO 175-2010 and client’s requirements

Medium: 35%(m/m) HCI(AR)

Method: Immersion method

Temperature: Room temperature

Test time: 48h

No visisble change

4

Sulfuric acid resistance

With reference to ISO 175-2010 and client’s requirements

Medium: 30%(m/m) H2SO4(AR)

Method: Immersion method

Temperature: Room temperature

Test time: 48h

No visisble change

5

Alikali resistance

With reference to ISO 175-2010 and client’s requirements

Medium: 40% (m/m) NaOH(AR)

Method: Immersion method

Temperature: Room temperature

Test time: 48h

No visible change.

6

Density

ISO 1183-1:2012     Method A

Abosolute alcohol, 23±0.5℃

1.799g/cm3

7

Flexural strength

ISO 178:2010/Amd.1:2013

Method A

Specimen:100x10.96x3.12mm

Testing speed: 1mm/min

Span: 50mm

41.3MPa

8

Flexural modulus

4520MPa

9

Charpy unnotched impact strength

ISO 179-1: 2010

Specimen: ISO 179-1/1Eu

Specimen thickness:3.13mm

The capcaity of the pendulum: 5J

Impact speed: 2.90m/s

Span: 62mm

38Kj/M2

C(complete break)

10

Vicat softening temperature

ISO 306:2004 Method B50

Specimen thickness: 3.01mm

Rate of temperature: 50℃/h

77.3℃

11

Tensile strength

ISO 527-1:2012 and ISO 527-2:2012

Specimen: Type 1B

Specimen thickness:3.05mm

Testing speed: 5mm/min

Grip separation:115mm

20.3MPa

12

Nominal tensile strain at break

13%

13

Impact resistance

GB/T 8814-2004 Section 5.7 and 6.7

Precondition:-10℃,1h→

Take out and do test within 10s.

Specimen thickness:3.02mm

Geometry: H.25

Strike weight: 1.0kg

Span: 200mm

Number of specimens tested:10

Number of spcimen breakage:0

14

Dimensional change

With reference to ASTM D1204-08 and client’s requirement

Condition: 100℃,60min→

23±2℃,50±5%RH,1h

Specimen: 25x25cm

Medium: Talcum powder

X drection

-0.7%

Y direction

-1.3%

15

Oxygen Index

ISO 4589-1: 1996 and ISO 4589-2: 1996/Amd.1:2005

Specimen: Type III

Specimen thickness: 3.2mm

Ignition procedure: Method A

32.8%

16

Horizontal burning test

UL 94-2013 Section 7

Specimen: 126x13.4x3.0mm

Conditioning: 23±2℃, 50±5%RH, 48h

HB

17

20mm Vertiacal burning test

UL 94-2013 Section 8

Specimen: 126x13.4x3.0mm

V-1

18

Burning test

DIN 4102-1:1998-05

See appendix1

The sample tested met the requirements of class B2

contact us

contact-email
contact-logo

Foshan Chancheng Xingfa Tile Industry Co.,Ltd

We provide high-quality products & services to our clients

看不清,请点击我!

If you would like to leave us a comment please go to contact us

Telphone: +86-757-85330625

email: info@upvcsupplier.com

contact-clo

 

top